Punches 86°

1233>
Cod. A R H TM L L2
1233 86 0.8 195 40 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)

Punches 86°

1233
Cod. A R H TM L L2
1234 86 0.6 195 30 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)

Punches 86°

1235
Cod. A R H TM L L2
1235 86 0.8 195 100 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)

Punches 60°

1236
Cod. A R H TM L L2
1236 60 0.8 195 40 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)

Punches 28°

1237
Cod. A R H TM L L2
1237 28 3 195 100 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)

Punches 28°

1238
Cod. A R H TM L L2
1238 28 1 195 80 500 550

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (550)