Euro Beyeler punches 90°

1201
Cod. A R H TM L L1 L2
1201 90 0.6 95 20 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 90/88°

1202
Cod. A R H TM L L1 L2
1202 90 0.8 95 100 500 1000 1100
1203 88 0.8 95 100 500 1000 1100
1204 88 2 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 88°

1205
Cod. A R H TM L L1 L2
1205 88 0.8 89.64 60 500 1000 1100
1206 88 2 89.97 60 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 88°

1202
Cod. A R H TM L L1 L2
1207 88 0.8 104.5 50 500 1000 1100
1208 88 2 103.97 50 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 30°

1209
Cod. A R H TM L L1 L2
1209 30 0.6 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 86°

1285
Cod. A R H TM L L1 L2
1285 86 1 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 80°

1286
Cod. A R H TM L L1 L2
1286 80 1 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 60°

1287
Cod. A R H TM L L1 L2
1287 60 3 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)

Euro Beyeler punches 90/88°

1288
Cod. A R H TM L L1 L2
1202 90 0.8 95 100 500 1000 1100
1203 88 0.8 95 100 500 1000 1100
1204 88 2 95 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Fractional sets (1100)