1026Punches 60°

Cod. A R H Tm L L1 L2
1026 60 0.8 67 80 415 835 805
1027 60 2 67 80 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

1162Punches 60°

Cod. A R H Tm L L1 L2
1162 60 0.8 85 40 415 835 805

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding

1191Punches 60°

Cod. A R H Tm L L1 L2
1191 60 0.8 115 60 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

1163Punches 60°

Cod. A R H Tm L L1 L2
1163 60 0.8 130 40 415 835 805

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding

1190Punches 60°

Cod. A R H Tm L L1 L2
1190 60 0.8 160 40 415 835 805

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding

1272Punches 60°

Cod. A R H Tm L L1 L2
1272 60 0.8 115 40 415 835 805

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding

1271Punches 60°

Cod. A R H Tm L L1 L2
1271 60 0.8 115 50 415 835 805

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding

1032Punches 60°

Cod. A R H Tm L L1 L2
1032 60 6 65 100 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

1283Punches 60°

Cod. A R H Tm L L1 L2
1283 60 10 115 100 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

1284Punches 60°

Cod. A R H Tm L L1 L2
1284 60 0.8 135 70 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

 

1053Punches 45°

Cod. A R H Tm L L1 L2
1053 45 6 100 100 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

1054Punches 45°

Cod. A R H Tm L L1 L2
1054 45 6 50 100 415 835 805

Constructed in steel C45, wear parts induction hardened up to 55-60 HRc and finished in grinding

 