Beleyer RF-A punches 88°

1227
Cod. A R H TM L L1 L2
1227 88 1.5 175 50 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Beleyer RF-A punches 88°

1228
Cod. A R H TM L L1 L2
1228 88 1 175 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Beleyer RF-A punches 88°

1229
Cod. A R H TM L L1 L2
1229 88 1 175 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Beleyer RF-A punches 30°

1230
Cod. A R H TM L L1 L2
1230 30 1 175 80 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Beleyer RF-A punches 30°

1231
Cod. A R H TM L L1 L2
1231 30 3 175 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Beleyer RF-A punches 30°

1232
Cod. A R H TM L L1 L2
1232 30 1 175 80 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)