Dies 90°

3102
Cod. V A R H S T Rf TM L L1 L2
3101 6 90 0.4 55 15 20 R0.5 100 500 1000 1100
3102 8 90 0.5 55 15 20 R0.5 100 500 1000 1100
3103 10 90 1.0 55 20 20 R0.5 100 500 1000 1100
3104 12 90 1.5 55 20 20 R0.5 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Dies 88°

3108
Cod. V A R H S T Rf TM L L1 L2
3106 10 88 1.0 55 20 20 R0.5 100 500 1000 1100
3107 12 88 1.5 55 20 20 R0.5 100 500 1000 1100
3108 16 88 2.0 55 30 30 R0.5 100 500 1000 1100
3109 20 88 2.0 55 30 30 R0.5 100 500 1000 1100
3110 24 88 3.0 55 40 40 R0.5 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Dies 85°

3111
Cod. V A R H S T Rf TM L L1 L2
3111 32 85 4.0 55 50 50 R3.0 100 500 1000 1100
3112 40 85 4.0 55 50 50 R4.0 100 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Dies 60°

3111
Cod. V A R H S T Rf TM L L1 L2
3113 40 60 5.0 55 55 55 R5.0 80 500 1000 1100
3179 50 60 5.0 55 70 70 P15.0 100 500 1000 1100
3114 60 60 7.0 65 80 80 P15.0 60 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)

Dies 30°

3118
Cod. V A R H S T Rf TM L L1 L2
3115 6 30 0.6 55 15 20 R1.0 35 500 1000 1100
3116 8 30 0.8 55 15 20 P2.0 35 500 1000 1100
3117 10 30 1.0 55 20 20 P2.0 50 500 1000 1100
3118 12 30 1.5 55 20 20 P2.0 40 500 1000 1100
3119 16 30 2.0 55 30 30 P5.0 45 500 1000 1100
3120 20 30 2.5 55 35 35 P5.0 50 500 1000 1100
3121 24 30 3.0 55 40 40 P8.0 50 500 1000 1100
3122 32 30 4.0 60 60 60 P10.0 50 500 1000 1100

Constructed in steel C45 quenched (resistance 850-1000 N/mm2), wear parts induction hardened up to 55-60 HRc and finished in grinding
Sectional sets (1100)